FAST MELTING SILICON
Used to adjust the content of Silicon element in the manufacture of high quality Aluminum Alloys. The product can be direct added and rapid dissolution at normal casting-house operating temperatures.
Specifications
Content of Si: 95% Recovery rate: over 90%
Instruction
In order to achieve high element recovery, 740℃ is recommended minimum adding temperature. After skimming the slag, the products can be direct added into the furnace dispersedly. Waiting for 5 minutes and then mix round about 5 minutes.
Remark: To prevent deposit, division of the adding procedure in several times is required if the target amount is over 3%.
Packing and Storage
10KGS in one kraft-paper bag.
Store in a dry and cool place
Advangtages
- The dissolution speed is extremely fast, the reaction is rapid, and the time is saved.
- The content is as high as 95%, which can precisely control the amount of silicon added, and quickly configure any proportion of aluminum-silicon alloy.
- It is very convenient to use, just put it on the surface of the aluminum liquid, press it in and stir it. The recovery rate is greater than 90%.
- An ideal replacement product for aluminum-silicon intermediate alloys. It eliminates a large number of inclusions and harmful substances that are easily brought into aluminum-silicon alloys, and avoids the use of waste and miscellaneous aluminum to prepare aluminum-silicon alloys, which is difficult to control the quality of the final aluminum alloy.
- Significantly reduce the melting temperature, greatly reduce the melting time, and greatly reduce the cost of alloy ingredients.